310 310s Stainless Steel Wire Mesh fls-57 manufacturer from China Hebei Fulang Metal Wire Mesh Product Co.,Ltd

Payment Terms:	T/T,L/C,Paypal
Place of Origin:	Hebei, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: fls-57

Production Capacity: 300m2 per month

Delivery Date: 15days after received the d...

Type: Woven

Brand Name: Fulangsi

Means of Transport: Ocean,Land,Air

Packing: Water proofed paperplastic ...

Application: Filter

Material: Others

Mesh Size: 100mesh

310 310s Stainless Steel Wire Mesh
1.High quality,lowest price
2.Made as customer's require
3.Fast delivery
4.Factory

310 310s Stainless Steel Wire Mesh,Stainless steel wire mesh

Stainless Steel 310 Mesh has good strength as well as excellent corrosion resistance at the high temperature up to 2100of or 1149oC.

Consisting of significant content of chromium and nickel, Stainless Steel 310 Mesh provides better performance in resisting general and localized corrosion than SS 304 mesh. It is a proven material for high temperature filtration elements.

Features of 310s stainless steel wire mesh

310S stainless steel(2520), due to high content of Ni and Cr, it is with good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance. The maximum service temperature is 1200℃

310/310S Stainless Steel Wire Mesh Chemistry

Element	Cr	Ni	C	Si	Mn	P	S	Mo	Cu	Fe
SS 310	24 – 26 %	19.2 – 22 %	0.25 %	1.50 %	2 %	0.045 %	.03 %	0.75 %	0.50 %	Bal
SS 310S	24 – 26 %	19.2 – 22 %	0.25 %	1.50 %	2 %	0.045 %	.03 %	0.75 %	0.50 %	Bal

Stainless Steel 310/310S Mesh Property Data

Density (lb / cu. in.)	0.289
Specific Gravity	7.9
Specific Heat (Btu/lb/Deg F – [32-212 Deg F])	0.12
Electrical Resistivity (microhm-cm (at 68 Deg F))	468
Melting Point (Deg F)	2650
Modulus of Elasticity Tension	30
Mean coefficient of thermal expansion	8.8 x 10(6)per oF, 15 x 10(6) per oC
Elastic modulus	29 Psi x 10(6) or 200 GPa
Yield strength 0.2 percent offset	45 ksi or 310 MPa
Tensile strength	95 ksi or 655 MPa
Reduction of area %	69 %
Hardness Rockwell B	85